1.Keemiline koostisjaMehaanilised omadused (InQuenched& TemperedState):
Materjal | 5140 | ||
Keemiline koostis | Mehaanilised omadused (InQuenched& TemperedState) | ||
C | 0.37-0.44 | Tõmbepikkus (MPA) | 980 |
Si | 0.17-0.37 | Saagisjõud (MPA) | 785 |
Mn | 0.50-0.80 | Pikenemine (δ5 /%) | 9 |
Kr | 0.80-1.10 | Pindala vähendamine (ψ /%) | 45 |
Mo | 0.15-0.25 | Mõju (J) | 47 |
P | ≤0.035 | Kõvadus | ≤207HB |
S | ≤0.035 | ||
Cu | ≤0.30 | ||
Ni | ≤0.30 | ||
2.Ssamaväärse astmega& samaväärsed terasmaterjalid:
USA | Jaapani keel | Gemany | Briti | Prantsusmaa | Rahvusvaheline | Hiina keel |
ASTM& AISI& SAE | JIS | LÕPP | ENBS | ENNF | ISO | GB |
5140 | SCr440 | 41Cr4 (1,7035) | Cr4 | ------ | 40Cr |