AISI H10 /din 1.2365 32CrMoV12-28 h10 jis skd7 terasvarras
1,2365 terasest bohler
TÖÖRIISTATERAS KUUMTÖÖTLEMISEKS 32CRMOV12-28, 1.2365, AISI H-10 VASTAVALT ISO 4957.
| Standard | Terase klass | ||||||||
|---|---|---|---|---|---|---|---|---|---|
| Keemilise koostise protsent | |||||||||
| C: | Mn: | Si: | P: | S: | Kr: | Mo: | V: | ||
| ISO | 1.2365 - 32CrMoV12-28 | ||||||||
| 0.28 - 0.35 | 0.15 - 0.45 | 0.1 - 0.4 | <0.03 | <0.02 | 2.7 - 3.2 | 2.5 - 3.0 | 0.4 - 0.7 | ||
| DIN | 32CrMoV3-3 - 32 CrMoV 3-3 | ||||||||
| 0.28 - 0.35 | 0.15 - 0.45 | 0.1 - 0.4 | <0.03 | <0.03 | 2.7 - 3.2 | 2.6 - 3.0 | 0.4 - 0.7 | ||
| PN | WLV | ||||||||
| 0.25 - 0.35 | 0.25 - 0.50 | 0.15 - 0.40 | <0.03 | <0.03 | 2.5 - 3.0 | 2.5 - 3.0 | 0.4 - 0.6 | ||
| ET | 30CrMoV12-11 | ||||||||
| 0.25 - 0.35 | 0.15 - 0.45 | 0.1 - 0.4 | <0.03 | <0.03 | 2.5 - 3.5 | 2.5 - 3.0 | 0.4 - 0.7 | ||
| ASTM | AISI H-10 - UNS T20810 | ||||||||
| 0.35 - 0.45 | 0.2 - 0.7 | 0.8 - 1.25 | <0.03 | <0.03 | 3.00 - 3.75 | 2.0 - 3.0 | 0.25 - 0.75 | ||
| GOST | 3H3M3F - | ||||||||
| 0.27 - 0.34 | 0.2 - 0.5 | 0.1 - 0.4 | <0.03 | <0.03 | 2.8 - 3.5 | 2.5 - 3.0 | 0.4 - 0.6 | ||
1.2365, 32CrMoV12-28, X32CrMoV3-3 - spetsifikatsioonid ja rakendused
Tööriistateras kuumtöötlemiseks, kasutatakse pressmaatriksite, stantside, värviliste metallide valamise vormide, tööriistade ja templite tootmiseks pressimiseks ja stantsimiseks. Seda iseloomustab kõrge karastamine, suurepärane soojusjuhtivus, vastupidavus temperatuurierinevusele vesijahutuse ajal ja vastupidavus karastamisele. See saavutab kõvaduse taseme 52 HRC.
Terase 1,2365, 32CrMoV12-28 mehaanilised omadused
Karedus pluss A tarnetingimuses:<229 HB Hardness in +A+C delivery condition: <249 HB Hardness after hardening: 52 HRC Hardness after hardening and tempering at temperature: 300℃ = 47.2 HRC 350℃ = 47.6 HRC 400℃ = 48.5 HRC 450℃ = 50.0 HRC 500℃ = 51.7 HRC 550℃ = 51.9 HRC 600℃ = 49.0 HRC Thermal conductivity, λ: 36 W * m-1 * K-1 Linear expansion coefficient, α: 12.4 * 10-6 K-1
Terase 1,2365, 32CrMoV12-28 kuumtöötlus
Pehmendav lõõmutamine 740 - 770 kraadi juures Reljeefne lõõmutamine 600 - 700 kraadi juures Kõvenemine 1030 - 1050 kraadi juures Karastus 450 - 550 kraadi juures Nitriidimine 470 - 550 kraadi juures
2. Toote kasutusvaldkonnad:
Meie tooteid on kasutatud igasugustes valdkondades, nagu lennundus, lennundus, navigatsioon, tuumaenergia, keemiatööstus,
elektrooniline teave, masinate tootmine, naftakeemia, autotööstus, instrumendid ja arvestid, side, transport ja meditsiiniinstrumendid jne.
3. Sarnased terase klassid ja samaväärsed terasmaterjalid:
|
USA |
Jaapani |
Saksamaa |
Briti |
Prantsusmaa |
kuumtöötlus |
hiina keel |
|
ASTM&AISI&SAE |
JIS |
ET DIN |
ET BS |
ET NF |
ISO |
GB |
|
AISI H10 |
1.2365 |
------ |
||||
1.2365 terasest bohler ja latt tehasest
Kuum tags: 1.2365 terasest bohler jis skd7, Hiina, tootjad, tarnijad, tehas